2000系列洛氏硬度计
2000系列洛氏硬度计具有最好的深度测量精度和分辨率，该硬度计配备了独有的闭环式电子力学传感装置和高精度的“同轴”深度测量技术，使硬度测试更加快捷，精密和可靠。采用一键式操作，使用方便。人性化设计的LCD操作面板进行方法设定和参数设置。2000洛氏硬度计提供6-14英寸范围的测试空间以满足不同尺寸试样测试要求，产品分为普通、表面和双洛氏3种型号，涵盖所有普通和表面洛氏硬度标尺（15，30，45，60，100，150总试验力）。
Series Models
|
|
Capabilities
|
|
|
|
Regular
|
Superficial
|
|
Rockwell 2000R
|
Yes
|
|
|
Rockwell 2000S
|
|
Yes
|
|
Rockwell 2000T
|
Yes
|
Yes
|
规格
|
|
2000R
|
2000S
|
2000T
|
|
Hardness Capabilities
|
Regular
|
Superficial
|
Regular and Superficial
|
|
硬度标尺
|
A, B, C, D, E, F, G, H, K, L, M, P, R, S, V
|
15N, 30N, 45N, 15T, 30T, 45T, 15W, 30W, 45W, 15X, 30X, 45X, 15Y, 30Y, 45Y
|
A,B, C, D, E, F, G, H, K, L, M, P, R, S, V, 15N, 30N, 45N, 15T, 30T, 45T, 15W, 30W, 45W, 15X, 30X, 45X, 15Y, 30Y, 45Y
|
|
初试验力
|
10 Kg
(98.07 N)
|
3 Kg
(29.42 N)
|
3, 10 Kg
(29.42, 98.07 N)
|
|
试验力
|
60, 100, 150 Kg
(588.4, 980.7, 1471 N)
|
15, 30, 45 Kg
(147.1, 294.2, 441.3 N)
|
15, 30, 45, 60, 100, 150 Kg
(147.1, 294.2, 441.3, 588.4, 980.7, 1471 N)
|
|
Test Load Control
|
Closed-Loop Electronic Load Cell
|
|
试验力加载
|
Automatic (loading, dwell, unloading)
|
|
保持时间
|
1 to 99 sec
|
|
Test Cycle Type
|
Motorized (Manual preload, auto trip, auto brake)
|
|
最大允许试件高度
|
Size 1: 153 mm (6 in),
Size 2: 255 mm (10 in),
Size 3: 355 mm (14 in)
|
|
试样照明
|
Flexible Fiber Optic
|
|
符合标准
|
ASTM E18, ASTM D785, ASTM B294, ISO 6508, JIS Z2245, GB/T 230
|
|
标尺转换
|
ASTM E140
|
|
数理统计
|
Number of Tests, Mean, Standard Deviation, Range Min Max
|
|
语言
|
English, German, French
|
|
Data Memory
|
999 test per hardness scale
|
|
数据输出
|
RS-232
|
|
分辨率
|
0.1 or .01 HR (adjustable)
|
|
中心线处深度
|
216 mm (8.5 in) at the top, 155 mm (6.13 in) at the bottom
|
|
显示
|
LCD
|
|
机器尺寸
|
Width: 343 mm (13.5 in)
Depth: 590 mm (23.2 in)
Height: 1232 mm (48.5 in) Size 2, 1334 mm (52.2 in) Size 3
|
|
最大试样重量
|
100 Kg (220 lb)
|
|
机器重量
|
Size 1: 100 kg (220 lb), Size 2: 107 Kg (232 lb), Size 3: 113 Kg (250 lb)
|
|
电源
|
100, 110, 220, 240 VAC options, 47 to 63 Hz single phase
|
|
应用
|
Steels, Coppers, Cast Irons, Thin Materials, Shallow and Deep Case Hardened Materials
|
|